HS18-0-1, hot-rolled, forged, cold-drawn steel bars are delivered in annealed state , hot-rolled, forged steel bars are delivered in annealing + other processing methods (peeling, light drawing, grinding or polishing, etc. ) Delivery after processing.
Chinese name HS18-0-1 Material name High speed tool steel
Grade HS18-0-1 Standard EN ISO 4957-1999
Catalog
![HS18-0-1, hot-rolled, forged, and cold-drawn steel bars are delivered in an annealed state. Hot-rolled and forged steel bars are delivered after annealing + other processing methods (peeling, light drawing, grinding or polishing, etc.) goods. - DayDayNews](https://cdn-dd.lujuba.top/img/loading.gif)
Chemical composition
Editorial report
Carbon C: 0.73~ 0.83
Silicon Si: 0.20~0.45
Manganese Mn: 0.10~0.40
Sulfur S: ≤0.030
Phosphorus P: ≤0.030
Chromium Cr: 3.80~4.50
Vanadium V: 1.00~1. 20
Tungsten W: 17.20~18.70
Mechanics Performance
Editor broadcast
Hardness: Delivery hardness: (other processing methods) ≤ 269HB; (annealing) ≤ 255HB. Sample heat treatment system and quenching and tempering hardness: ≥63HRC
Heat treatment specifications and metallographic structure:
Heat treatment specifications: quenching, 820~870℃ preheating, 1270~1285℃ ( salt bath furnace ) or 1270~1285℃ ( Box-type furnace) heating, oil cooling, tempering at 550~570℃ twice, 1 hour each time.
Delivery status
Editor report
Hot-rolled, forged, and cold-drawn steel bars are delivered in an annealed state, and hot-rolled and forged steel bars are processed by annealing + other processing methods (peeling, light drawing, grinding or polishing, etc.) post delivery