Insulated glass does not significantly absorb visible light, but instead absorbs near-infrared light that generates a large amount of heat, which can reduce the temperature to around 3℃-6℃. Because of its characteristics such as heat insulation, energy saving and environmental protection, it is widely used in commercial buildings, hotels, hotels and other fields. Insulated glass does not significantly absorb visible light, but instead absorbs near-infrared light that generates a large amount of heat, which can reduce the temperature to around 3℃-6℃. Because of its characteristics such as heat insulation, energy saving and environmental protection, it is widely used in commercial buildings, hotels, hotels and other fields. GB/T 29501-2013 Insulated coating glass testing project: Test project Indicator requirements for exposure Indicator requirements for non-exposed Testing order Method physical performance adhesion ≤1 level GB/T 9286 hardness ≥3H ≥H ≥H GB/T 6739 Water resistance / GB/T 1733 acid rain resistance / GB/T 9274 alkali resistance / GB/T 9274 temperature degeneration no exception JC 846 combust resistance combustion rate is not greater than 100mm/min combustion rate is not greater than 100mm/min JC 846 Color uniformity ≤3.0 ≤3.0 ≤3.0 GB/T 18915.1 UV aging resistance Appearance: No bubbles, no peeling, no cracks, no obvious discoloration Powdering: Level 0 adhesion: Level 0 Appearance: No bubbles, no peeling, no cracks, no obvious discoloration Powdering: Level 0 Adhesion: ≤ Level 1 GB/T 23987 heat insulation temperature difference ≥7℃ ≥7℃ GB/T 29501 level 68h No exception 68h no exception 68h no exception
GB/T 29501-2013 Insulated coating glass detection project:
Test project | Type I | Type II | Type II | Type I | Test method |
optical performance | |||||
visible light transmission ratio | ≥40% | ≥50% | ≥60% | GB/T 2680 | |
visible light transmission deviation | ≤3% | ≤3% | ≤3% | ≤3% | GB/T 2680 |
visible light reflection ratio | ≤10% | ≤10% | ≤10% | ≤10% | GB/T 2680 |
visible light reflection ratio deviation | ≤3% | ≤3% | ≤3% | ≤3% | GB/T 2680 |
occlusion coefficient | ≤0.55 | >0.55, ≤0.65 | >0.65, ≤0.80 | GB/T 2680 | |
occlusion coefficient deviation | ≤0.03 | ≤0.03 | ≤0.03 | ≤0.03 | GB/T 2680 |
ultraviolet transmission ratio | ≤ 10% | ≤ 10% | ≤ 10% | GB/T 2680 | |
visor 0mdl0 |
≥95%
≥95%
GB/T 2680
GB/T 2680-1994 Architectural glass Visible light transmission ratio, direct solar light transmission ratio, total solar energy transmission ratio, ultraviolet transmission ratio and related window glass parameters
ISO 9050:2003 Architectural glass Visible light transmission ratio, direct solar light transmission ratio, total solar energy transmission ratio, ultraviolet transmission ratio and related window glass parameters
EN 410:2011 Architectural glass-glass optical performance test method
ASTM E903 Methods for testing sunlight absorption ratio, reflection ratio and transmission ratio by integral sphere method
Guangzhou General Testing Technology Service Co., Ltd. Type inspection products:
Ceramic tiles , stone, cement fiberboard, calcium silicate board , wood plastic floor , artificial board, aluminum plastic board, high floor, light partition board , gypsum board, light steel dragon Bone , ceiling, building glass, door and window hardware, SPC floor, plywood and other building materials products...
Guangzhou General Testing Technology Service Co., Ltd. Testing project:
Mechanical performance test, Thermal Performance test, optical performance test, electrical performance test, aging performance, composition analysis, fire resistance, fire resistance limit, salt spray corrosion test, mildew resistance, antibacterial, antiviral test, etc....